Low temperature cyanate ester system. Initial cure (70°C/158°F) for 20 hours. Out life at (21°C/70°F) 3 days. Max dry Tg after post-cure (330°C/626°F) | Good dimensional and thermal stability to (250°C/482°F), withstanding spikes to (330°C/626°F). Good FST performance, low out-gassing and good dielectric properties. Out Time (days): 3 | Service Temp: 482 (250) | Cure Flex: 158 - 482 (70 - 250) | Process: Autoclave | TG: 626 (330)

Low temperature, autoclave cure, epoxy tooling system. Minimum cure temperature (30°C/86°F). Out life at (21°C/70°F) 3 days. Maximum Tg after post-cure (205°C/401°F). | Tacky, first generation system Product Form: epoxy prepreg | Out Time (days): 3 | Temp: 356 (180) | Cure Flex: 70 hours at 86 (30) | Process: autoclave

Low temperature, autoclave cure epoxy tooling system. Minimum cure temperature (30°C/86°F). Out life at (21°C/70°F)2 days. Maximum Tg after post-cure (180°C/356°F). | Tacky, first generation system Product Form: epoxy prepreg | Out Time (days): 3-4 | Temp: 350 (177) | Cure Flex: 168 hours at 68 (20) | Process: autoclave

Low temperature, autoclave cure, epoxy tooling system. Minimum cure temperature (40°C/104°F), Out life at (22°C/70°F) 6 days, Maximum Tg after post-cure (205°C/401°F). | Tacky, first generation system Product Form: epoxy prepreg | Out Time (days): 6 | Temp: 356 (180) | Cure Flex: 70 hours at 104 (40) | Process: autoclave

Low temperature, autoclave cure, epoxy tooling system. Minimum cure temperature (45°C/113°F). Out life at (21°C/70°F) 4 days. Maximum Tg after post-cure (180°C/392°F). | Excellent tack and handling. Compatible with DForm® technology Product Form: epoxy prepreg | Out Time (days): 4 | Temp: 356 (180) | Cure Flex: 8 hours at 140 (60) | Process: autoclave

Toughened low temperature, vacuum bag processable, epoxy tooling system. Minimum cure temperature (80°C/176°F). Out life at (21°C/70°F) 21 days. Maximum Tg after post-cure (180°C/356°F). | For manufacture of caul plates through various ZPREG® selective impregnation formats Product Form: epoxy prepreg | Out Time (days): 21 | Temp: 356 (180) | Cure Flex: 176-248 (80-120) | Process: vacuum, autoclave

Low temperature, autoclave cure, epoxy tooling system. Minimum cure temperature (35°C/95°F). Out life at (21°C/70°F) 2 days. Maximum Tg after post-cure (210°C/410°F). | Lower tack at high ambient temperatures Product Form: epoxy prepreg | Out Time (days): 2 | Temp: 356 (180) | Cure Flex: 40 hours at 95 (35) | Process: autoclave

Low temperature, autoclave cure, epoxy tooling system. Minimum cure temperature (55°C/131°F). Out life at (21°C/70°F) 8 days. Maximum Tg after post-cure (210°C/410°F). | Lower tack at high ambient temperatures. Can be used with LTF318B controlled flow surface ply and syntactic ply for a high quality surface using low pressure. Product Form: epoxy prepreg | Out Time (days): 8 | Temp: 356 (180) | Cure Flex: 20 hours at 131 (55) | Process: autoclave

Low temperature, vacuum processable, epoxy system. Minimum cure (50°C/122°F). Out life at (21°C/70°F) 2 days. Maximum Tg after post-cure (125°C/257°F). | A surfacing ply for other LTM systems, it enables a near flaw-free surface and low void laminates under vacuum bag conditions. Process: vacuum | TG: 257 (125) | Viscosity: medium

Low temperature, vacuum processable, epoxy series. Minimum cure (50°C/122°F). Out life at (21°C/70°F) 2-5 days depending on variant. Maximum Tg after post-cure (130°C/266°F). | LTM26 and 26EL offer relatively good clarity and UV stability. LTM26ELFR is fire-retarded to meet JAR25.283 Vertical Burn Process: press, autoclave | TG: 248 - 257 (120 - 125) | Viscosity: medium

Low temperature, vacuum bag processable, epoxy tooling system. Minimum cure temperature (65°C/149°F). Out life at (21°C/70°F) 21 days. Maximum Tg after post-cure (170°C/338°F). | For tooling manufactured in or out of autoclave, compatible with various ZPREG® formats and surface films Product Form: epoxy prepreg | Out Time (days): 21 | Temp: 302 (150) | Cure Flex: 16 hours at 150 (65) | Process: vacuum

Process: autoclave, press | TG: 410 (210) | Viscosity: lov